Colloidal interactions in an alternate make cheese : a thesis presented in partial fulfilment of the requirements for the degree of Doctor of Philosophy in Food Technology at Massey University, (Manawatū), New Zealand

dc.contributor.authorLuo, Jing
dc.date.accessioned2018-06-05T19:35:36Z
dc.date.available2018-06-05T19:35:36Z
dc.date.issued2017
dc.description.abstractThe role of emulsion structure and interactions on the material and technical functionality of an alternate make cheese (AMC) was investigated. Lab scale cheese samples (25 g comprising 23 wt.% fat and 20 wt.%) were prepared by recombining model emulsions with a separate protein phase under controlled temperature, shear speed and residence time in a rapid visco analyser (RVA). Sodium caseinate and Tween 20 were used respectively to stabilize fat globules for the model emulsions. Preliminary experiments were carried out for samples prepared using either calcium caseinate or sodium caseinate as protein phase. Structural characterisation of samples showed emulsion structure and distribution within these phases to be dependent on protein type. It was inferred that the calcium from calcium caseinate matrix modified the interfacial layer of the emulsions stabilised by sodium caseinate, as indicated by the increased fat globule size distribution after cheese making. In comparison, the size of fat globules covered with sodium caseinate appeared relatively stable in cheese produced form cheese curd. Based on these observations, caseinates were subsequently replaced by cheese curd as the protein phase for the remainder of the study. For cheese samples prepared with low fat cheese curd, fat droplets stabilised with sodium caseinate were hypothesised as binding with the surrounding protein matrix, and thereby these fat globules could be considered as ‘active fillers’. Confocal laser scanning microscopy supported this hypothesis showing homogeneously dispersed fat droplets within the protein network. This emulsion system did not show fat-protein phase separation in baking (170 °C 10 minutes) as droplets were prevented from coalescing as a consequence of entrapment within the protein phase. Fat globules covered with Tween 20 were hypothesised as behaving as ‘inactive fillers’, with the adsorbed layer not anticipated to form bonds with the surrounding protein network. Confocal and scanning electron microscopy instead showed localised domains of fat droplets within the protein structure that underwent partial coalescence on cooling of the cheese after manufacture. Cheeses comprising Tween stabilised droplets exhibited phase separation on baking and visible oil-off on the surface of cheese arising from extensive coalescence taking place within the localised regions of fat due to melting of the partially coalesced structures. Additional rheological analysis of cheeses was carried out to determine the effect of droplet-protein interactions on the material properties of the cheese samples. Notably, findings were presented in relation to a non-fat control cheese. Findings showed that, at temperatures below 30 °C when fat was crystallized, both inactive and active fillers had a higher relative modulus to the non-fat sample. However, at elevated temperature without fat crystals, inactive fillers resulted in a relative reduction in storage modulus when compared to the non-fat cheese, while active fillers increased relative storage modulus. Model cheeses prepared with either sodium caseinate or Tween 20 stabilised emulsions were then compared to cheese samples comprising non-homogenised cream as the emulsion phase. Structural analysis of samples determined that cheeses comprising fat globules stabilized with native milk fat globule membrane behaved in a manner analogous to samples prepared with the Tween stabilised emulsion, indicating the presence of inactive droplets. However, it was also observed that increasing the residence time of cheese production within the RVA caused a transition of the interaction behaviour of the emulsion from inactive to active, as evidenced by corresponding changes to structural, material and functional properties of the cheese. Further exploration of this transition determined that the mechanical work applied during cheese preparation was sufficient to homogenise fat droplets during extended shearing, resulting in a reduction to fat droplet size. Droplet homogenisation during shearing was also found to have disrupted the native milk fat globule membrane, allowing protein adsorption to take place. It was also determined that whey proteins were the predominant interfacial fraction adsorbed as a consequence of extended shearing, and were considered responsible for the transition of droplets from inactive to active. Combined findings have shown that the material and functional properties of an alternate make cheese composition could be strongly influenced by the interactions of the emulsion phase with the surrounding protein network. These interactions could, in turn, be manipulated through formulation and/or process design, providing greater control over product properties.en_US
dc.identifier.urihttp://hdl.handle.net/10179/13405
dc.language.isoenen_US
dc.publisherMassey Universityen_US
dc.rightsThe Authoren_US
dc.subjectCheeseen_US
dc.subjectColloidsen_US
dc.titleColloidal interactions in an alternate make cheese : a thesis presented in partial fulfilment of the requirements for the degree of Doctor of Philosophy in Food Technology at Massey University, (Manawatū), New Zealanden_US
dc.typeThesisen_US
massey.contributor.authorLuo, Jing
thesis.degree.disciplineFood Technologyen_US
thesis.degree.grantorMassey Universityen_US
thesis.degree.levelDoctoralen_US
thesis.degree.nameDoctor of Philosophy (PhD)en_US
Files
Original bundle
Now showing 1 - 2 of 2
Loading...
Thumbnail Image
Name:
01_front.pdf
Size:
218.48 KB
Format:
Adobe Portable Document Format
Description:
Loading...
Thumbnail Image
Name:
02_whole.pdf
Size:
5.27 MB
Format:
Adobe Portable Document Format
Description:
License bundle
Now showing 1 - 1 of 1
Loading...
Thumbnail Image
Name:
license.txt
Size:
3.32 KB
Format:
Item-specific license agreed upon to submission
Description: